Lithium metal secondary battery featuring an anode-protecting layer

ABSTRACT

Provided is a lithium secondary battery, comprising a cathode, an anode, and a porous separator or electrolyte disposed between the cathode and the anode, wherein the anode comprises: (a) an anode active layer containing a layer of lithium or lithium alloy, in a form of a foil, coating, or multiple particles aggregated together, as an anode active material; and (b) an anode-protecting layer of a conductive sulfonated elastomer composite, disposed between the anode active layer and the separator/electrolyte; wherein the composite has from 0.01% to 50% by weight of a conductive reinforcement material dispersed in a sulfonated elastomeric matrix material and the protecting layer has a thickness from 1 nm to 100 μm, a fully recoverable tensile strain from 2% to 500%, a lithium ion conductivity from 10 −7  S/cm to 5×10 −2  S/cm, and an electrical conductivity from 10 −7  S/cm to 100 S/cm.

FIELD OF THE INVENTION

The present invention relates to the field of rechargeable lithium metal battery having a lithium metal layer (in a form of thin lithium foil, coating, or sheet of lithium particles) as an anode active material and a method of manufacturing same.

BACKGROUND OF THE INVENTION

Lithium-ion and lithium (Li) metal cells (including Lithium-sulfur cell, Li-air cell, etc.) are considered promising power sources for electric vehicle (EV), hybrid electric vehicle (HEV), and portable electronic devices, such as lap-top computers and mobile phones. Lithium metal has the highest capacity (3,861 mAh/g) compared to any other metal or metal-intercalated compound (except Li_(4.4)Si) as an anode active material. Hence, in general, rechargeable Li metal batteries have a significantly higher energy density than lithium ion batteries.

Historically, rechargeable lithium metal batteries were produced using non-lithiated compounds having high specific capacities, such as TiS₂, MoS₂, MnO₂, CoO₂ and V₂O₅, as the cathode active materials, which were coupled with a lithium metal anode. When the battery was discharged, lithium ions were dissolved from the lithium metal anode and transferred to the cathode through the electrolyte and, thus, the cathode became lithiated. Unfortunately, upon cycling, the lithium metal resulted in the formation of dendrites that ultimately caused unsafe conditions in the battery. As a result, the production of these types of secondary batteries was stopped in the early 1990's giving ways to lithium-ion batteries.

Even now, cycling stability and safety concerns remain the primary factors preventing the further commercialization of Li metal batteries for EV, HEV, and microelectronic device applications. These issues are primarily due to the high tendency for Li to form dendrite structures during repeated charge-discharge cycles or an overcharge, leading to internal electrical shorting and thermal runaway. Many attempts have been made to address the dendrite-related issues, as briefly summarized below:

Fauteux, et al. [D. Fauteux, et al., “Secondary Electrolytic Cell and Electrolytic Process,” U.S. Pat. No. 5,434,021, Jul. 18, 1995] applied to a metal anode a protective surface layer (e.g., a mixture of polynuclear aromatic and polyethylene oxide) that enables transfer of metal ions from the metal anode to the electrolyte and back. The surface layer is also electronically conductive so that the ions will be uniformly attracted back onto the metal anode during electrodeposition (i.e. during battery recharge). Alamgir, et al. [M. Alamgir, et al. “Solid polymer electrolyte batteries containing metallocenes,” U.S. Pat. No. 5,536,599, Jul. 16, 1996] used ferrocenes to prevent chemical overcharge and dendrite formation in a solid polymer electrolyte-based rechargeable battery.

Skotheim [T. A. Skotheim, “Stabilized Anode for Lithium-Polymer Battery,” U.S. Pat. No. 5,648,187 (Jul. 15, 1997); U.S. Pat. No. 5,961,672 (Oct. 5, 1999)] provided a Li metal anode that was stabilized against the dendrite formation by the use of a vacuum-evaporated thin film of a Li ion-conducting polymer interposed between the Li metal anode and the electrolyte. Skotheim, et al. [T. A. Skotheim, et al. “Lithium Anodes for Electrochemical Cells,” U.S. Pat. No. 6,733,924 (May 11, 2004); U.S. Pat. No. 6,797,428 (Sep. 28, 2004); U.S. Pat. No. 6,936,381 (Aug. 30, 2005); and U.S. Pat. No. 7,247,408 (Jul. 24, 2007)] further proposed a multilayer anode structure consisting of a Li metal-based first layer, a second layer of a temporary protective metal (e.g., Cu, Mg, and Al), and a third layer that is composed of at least one layer (typically 2 or more layers) of a single ion-conducting glass, such as lithium silicate and lithium phosphate, or polymer. It is clear that such an anode structure, consisting of at least 3 or 4 layers, is too complex and too costly to make and use.

Protective coatings for Li anodes, such as glassy surface layers of LiI—Li₃PO₄—P₂S₅, may be obtained from plasma assisted deposition [S. J. Visco, et al., “Protective Coatings for Negative Electrodes,” U.S. Pat. No. 6,025,094 (Feb. 15, 2000)]. Complex, multi-layer protective coatings were also proposed by Visco, et al. [S. J. Visco, et al., “Protected Active Metal Electrode and Battery Cell Structures with Non-aqueous Interlayer Architecture,” U.S. Pat. No. 7,282,295 (Oct. 16, 2007); U.S. Pat. No. 7,282,296 (Oct. 16, 2007); and U.S. Pat. No. 7,282,302 (Oct. 16, 2007)].

Despite these earlier efforts, no rechargeable Li metal batteries have yet succeeded in the market place. This is likely due to the notion that these prior art approaches still have major deficiencies. For instance, in several cases, the anode or electrolyte structures are too complex. In others, the materials are too costly or the processes for making these materials are too laborious or difficult. Solid electrolytes typically have a low lithium ion conductivity, are difficult to produce and difficult to implement into a battery.

Furthermore, solid electrolyte, as the sole electrolyte in a cell or as an anode-protecting layer (interposed between the lithium film and the liquid electrolyte) does not have and cannot maintain a good contact with the lithium metal. This effectively reduces the effectiveness of the electrolyte to support dissolution of lithium ions (during battery discharge), transport lithium ions, and allowing the lithium ions to re-deposit back to the lithium anode (during battery recharge).

Another major issue associated with the lithium metal anode is the continuing reactions between electrolyte and lithium metal, leading to repeated formation of “dead lithium-containing species” that cannot be re-deposited back to the anode and become isolated from the anode. These reactions continue to irreversibly consume electrolyte and lithium metal, resulting in rapid capacity decay. In order to compensate for this continuing loss of lithium metal, an excessive amount of lithium metal (3-5 times higher amount than what would be required) is typically implemented at the anode when the battery is made. This adds not only costs but also a significant weight and volume to a battery, reducing the energy density of the battery cell. This important issue has been largely ignored and there has been no plausible solution to this problem in battery industry.

Clearly, an urgent need exists for a simpler, more cost-effective, and easier to implement approach to preventing Li metal dendrite-induced internal short circuit and thermal runaway problems in Li metal batteries, and to reducing or eliminating the detrimental reactions between lithium metal and the electrolyte.

Hence, an object of the present invention is to provide an effective way to overcome the lithium metal dendrite and reaction problems in all types of Li metal batteries having a lithium metal anode. A specific object of the present invention is to provide a lithium metal cell that exhibits a high specific capacity, high specific energy, high degree of safety, and a long and stable cycle life.

SUMMARY OF THE INVENTION

Herein reported is a lithium metal secondary battery, comprising a cathode, an anode, and an electrolyte or separator-electrolyte assembly disposed between the cathode and the anode, wherein the anode comprises: (a) a layer of lithium or lithium alloy (in the form of a foil, coating, or multiple particles aggregated together) as an anode active material; and (b) a thin anode-protecting layer comprising a conductive sulfonated elastomer composite having from 0.01% to 50% by weight of a conductive reinforcement material dispersed in a sulfonated elastomeric matrix material and said layer of conductive sulfonated elastomer composite has a thickness from 1 nm to 100 μm, a fully recoverable tensile strain from 2% to 500%, a lithium ion conductivity from 10⁻⁷ S/cm to 5×10⁻² S/cm, and an electrical conductivity from 10⁻⁷ S/cm to 100 S/cm when measured at room temperature, wherein the anode-protecting layer is disposed between the lithium or lithium alloy layer and the electrolyte or separator-electrolyte assembly layer. The foil or coating of lithium or lithium alloy may be supported by a current collector (e.g. a Cu foil, a Ni foam, a porous layer of nanofilaments, such as graphene sheets, carbon nanofibers, carbon nanotubes, etc.). A porous separator may not be necessary if the electrolyte is a solid-state electrolyte.

For defining the claims, the invented lithium metal secondary battery does not include a lithium-sulfur cell or lithium-selenium cell. As such, the cathode does not include sulfur, lithium polysulfide, selenium and lithium polyselenide.

The sulfonated elastomer is a high-elasticity material which exhibits an elastic deformation that is at least 2% (preferably at least 5%) when measured under uniaxial tension. In the field of materials science and engineering, the “elastic deformation” is defined as a deformation of a material (when being mechanically stressed) that is essentially fully recoverable upon release of the load and the recovery process is essentially instantaneous (no or little time delay). The elastic deformation is more preferably greater than 10%, even more preferably greater than 30%, further more preferably greater than 50%, and still more preferably greater than 100%.

Preferably, the conductive reinforcement material is selected from graphene sheets, carbon nanotubes, carbon nanofibers, carbon or graphite fibers, expanded graphite flakes, metal nanowires, conductive polymer fibers, or a combination thereof.

In some embodiments, the sulfonated elastomer composite preferably and more typically has a fully recoverable tensile strain from 5% to 300% (most typically from 10% to 150%), a thickness from 10 nm to 20 μm, a lithium ion conductivity of at least 10⁻⁵ S/cm, and an electrical conductivity of at least 10⁻³ S/cm when measured at room temperature on a cast thin film 20 μm thick.

Preferably, the sulfonated elastomeric matrix material contains a sulfonated version of an elastomer selected from natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, metallocene-based poly(ethylene-co-octene) (POE) elastomer, poly(ethylene-co-butene) (PBE) elastomer, styrene-ethylene-butadiene-styrene (SEBS) elastomer, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof.

These sulfonated elastomers or rubbers, when present without graphene sheets, exhibit a high elasticity (having a fully recoverable tensile strain from 2% to 800%). In other words, they can be stretched up to 800% (8 times of the original length when under tension) and, upon release of the tensile stress, they can fully recover back to the original dimension. By adding from 0.01% to 50% by weight of a conductive reinforcement material and/or a lithium ion-conducting species dispersed in a sulfonated elastomeric matrix material, the fully recoverable tensile strains are typically reduced down to 2%-500% (more typically from 5% to 300% and most typically from 10% to 150%).

The conducting reinforcement material is preferably in a filamentary or sheet-like form, such as a nanotube, nanofiber, nanowire, nanoplatelet, or nanodisc. In some embodiments, the conductive reinforcement material is selected from graphene sheets, carbon nanotubes, carbon nanofibers, carbon or graphite fibers, expanded graphite flakes, metal nanowires, conductive polymer fibers, or a combination thereof. These are electron-conducting materials and the sulfonated elastomer matrix is a lithium ion- and sodium ion-conducting material. By combining such a sulfonated elastomer and a conducting reinforcement, one obtains a composite that is both electron conducting and ion-conducting and capable of allowing electrons and lithium ions to migrate in and out of the particulate without much resistance.

The graphene sheets to be dispersed in a sulfonated elastomer matrix are preferably selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, nitrogenated graphene, hydrogenated graphene, doped graphene, functionalized graphene, or a combination thereof. The graphene sheets preferably comprise single-layer graphene or few-layer graphene, wherein the few-layer graphene is defined as a graphene platelet formed of less than 10 graphene planes. The carbon nanotubes (CNTs) can be a single-walled CNT or multi-walled CNT. The carbon nanofibers may be vapor-grown carbon nanofibers or electrospinning based carbon nanofibers (e.g. electrospun polymer nanofibers that are subsequently carbonized).

The conducting reinforcement material is preferably in a filamentary or sheet-like form, such as a nanotube, nanofiber, nanowire, nanoplatelet, or nanodisc. In some embodiments, the conductive reinforcement material is selected from graphene sheets, carbon nanotubes, carbon nanofibers, metal nanowires, conductive polymer fibers, or a combination thereof. These are electron-conducting materials and the sulfonated elastomer matrix is a lithium ion- and sodium ion-conducting material. By combining such a sulfonated elastomer and a conducting reinforcement, one obtains a composite that is both electron conducting and ion-conducting and capable of allowing electrons and lithium ions to migrate in and out of the particulate without much resistance.

In certain embodiments, the electrically conducting material may be selected from an electron-conducting polymer, a metal particle or wire (or metal nanowire), a graphene sheet, a carbon fiber, a graphite fiber, a carbon nanofiber, a graphite nanofiber, a carbon nanotube, a graphite particle, an expanded graphite flake, an acetylene black particle, or a combination thereof. The electrically conducting material (e.g. metal nanowire, nanofiber, etc.) preferably has a thickness or diameter less than 100 nm.

This sulfonated elastomer composite layer may be a thin film disposed against a lithium foil/coating layer surface or a thin coating deposited on the lithium foil/coating surface. It may be noted that lithium foil/coating layer may decrease in thickness due to dissolution of lithium into the electrolyte to become lithium ions as the lithium battery is discharged, creating a gap between the current collector and the protective layer if the protective layer were not elastic. Such a gap would make the re-deposition of lithium ions back to the anode impossible. We have observed that the instant sulfonated elastomer composite is capable of expanding or shrinking congruently or conformably with the anode layer. This capability helps to maintain a good contact between the current collector (or the lithium film itself) and the protective layer, enabling the re-deposition of lithium ions without interruption.

The sulfonated elastomer composite may further contain a lithium salt selected from lithium perchlorate (LiClO₄), lithium hexafluorophosphate (LiPF₆), lithium borofluoride (LiBF₄), lithium hexafluoroarsenide (LiAsF₆), lithium trifluoro-methanesulfonate (LiCF₃SO₃), bis-trifluoromethyl sulfonylimide lithium (LiN(CF₃SO₂)₂), lithium bis(oxalato)borate(LiBOB), lithium oxalyldifluoroborate (LiBF₂C₂O₄), lithium nitrate (LiNO₃), Li-fluoroalkyl-phosphates (LiPF₃(CF₂CF₃)₃), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.

At the anode side, preferably and typically, the sulfonated elastomer composite for the protective layer has a lithium ion conductivity no less than 10⁻⁵ S/cm, more preferably no less than 10⁻⁴ S/cm, and most preferably no less than 10⁻³ S/cm. Some of the selected sulfonated elastomer composites exhibit a lithium-ion conductivity greater than 10⁻² S/cm. In some embodiments, the sulfonated elastomer composite is an elastomer containing no additive or filler dispersed therein. In others, the sulfonated elastomer composite is an elastomer matrix composite containing from 0.1% to 50% by weight (preferably from 1% to 35% by weight) of a lithium ion-conducting additive dispersed in a sulfonated elastomer matrix material. In some embodiments, the sulfonated elastomer composite contains from 0.1% by weight to 10% by weight of a reinforcement nanofilament selected from carbon nanotube, carbon nanofiber, graphene, or a combination thereof.

In some embodiments, the sulfonated elastomer matrix material is selected from a sulfonated version of natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.

In some embodiments, the sulfonated elastomer composite further contains a lithium ion-conducting additive dispersed in a sulfonated elastomer composite matrix material, wherein the lithium ion-conducting additive is selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1 and 1<y<4.

The sulfonated elastomer composite may form a mixture, blend, co-polymer, or semi-interpenetrating network (semi-IPN) with an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof.

In some embodiments, the sulfonated elastomer composite may form a mixture, blend, or semi-IPN with a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a sulfonated derivative thereof, or a combination thereof. Sulfonation is herein found to impart improved lithium ion conductivity to a polymer.

The cathode active material may be selected from an inorganic material, an organic material, a polymeric material, or a combination thereof. The inorganic material may be selected from a metal oxide, metal phosphate, metal silicide, metal selenide, metal sulfide, or a combination thereof.

The inorganic material may be selected from a lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, or a combination thereof.

In certain preferred embodiments, the inorganic material is selected from a metal fluoride or metal chloride including the group consisting of CoF₃, MnF₃, FeF₃, VF₃, VOF₃, TiF₃, BiF₃, NiF₂, FeF₂, CuF₂, CuF, SnF₂, AgF, CuCl₂, FeCl₃, MnCl₂, and combinations thereof. In certain preferred embodiments, the inorganic material is selected from a lithium transition metal silicate, denoted as Li₂MSiO₄ or Li₂Ma_(x)Mb_(y)SiO₄, wherein M and Ma are selected from Fe, Mn, Co, Ni, V, or VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; and x+y<1.

In certain preferred embodiments, the inorganic material is selected from a transition metal dichalcogenide, a transition metal trichalcogenide, or a combination thereof. The inorganic material is selected from TiS₂, TaS₂, MoS₂, NbSe₃, MnO₂, CoO₂, an iron oxide, a vanadium oxide, or a combination thereof.

The cathode active material layer may contain a metal oxide containing vanadium oxide selected from the group consisting of VO₂, Li_(x)VO₂, V₂O₅, Li_(x)V₂O₅, V₃O₈, Li_(x)V₃O₈, Li_(x)V₃O₇, V₄O₉, Li_(x)V₄O₉, V₆O₁₃, Li_(x)V₆O₁₃, their doped versions, their derivatives, and combinations thereof, wherein 0.1<x<5.

The cathode active material layer may contain a metal oxide or metal phosphate, selected from a layered compound LiMO₂, spinel compound LiM₂O₄, olivine compound LiMPO₄, silicate compound Li₂MSiO₄, tavorite compound LiMPO₄F, borate compound LiMBO₃, or a combination thereof, wherein M is a transition metal or a mixture of multiple transition metals.

In some embodiments, the inorganic material is selected from: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, manganese, iron, nickel, or a transition metal; (d) boron nitride, or (e) a combination thereof.

The cathode active material layer may contain an organic material or polymeric material selected from poly(anthraquinonyl sulfide) (PAQS), a lithium oxocarbon, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA), poly(anthraquinonyl sulfide), pyrene-4,5,9,10-tetraone (PYT), polymer-bound PYT, quino(triazene), redox-active organic material, tetracyanoquinodimethane (TCNQ), tetracyanoethylene (TCNE), 2,3,6,7,10,11-hexamethoxytriphenylene (HMTP), poly(5-amino-1,4-dyhydroxy anthraquinone) (PADAQ), phosphazene disulfide polymer ([(NPS₂)₃]n), lithiated 1,4,5,8-naphthalenetetraol formaldehyde polymer, hexaazatrinaphtylene (HATN), hexaazatriphenylene hexacarbonitrile (HAT(CN)₆), 5-benzylidene hydantoin, isatine lithium salt, pyromellitic diimide lithium salt, tetrahydroxy-p-benzoquinone derivatives (THQLi₄), N,N′-diphenyl-2,3,5,6-tetraketopiperazine (PHP), N,N′-diallyl-2,3,5,6-tetraketopiperazine (AP), N,N′-dipropyl-2,3,5,6-tetraketopiperazine (PRP), a thioether polymer, a quinone compound, 1,4-benzoquinone, 5,7,12,14-pentacenetetrone (PT), 5-amino-2,3-dihydro-1,4-dyhydroxy anthraquinone (ADDAQ), 5-amino-1,4-dyhydroxy anthraquinone (ADAQ), calixquinone, Li₄C₆O₆, Li₂C₆O₆, Li₆C₆O₆, or a combination thereof.

The thioether polymer is selected from poly[methanetetryl-tetra(thiomethylene)](PMTTM), poly(2,4-dithiopentanylene) (PDTP), a polymer containing poly(ethene-1,1,2,2-tetrathiol) (PETT) as a main-chain thioether polymers, a side-chain thioether polymer having a main-chain consisting of conjugating aromatic moieties, and having a thioether side chain as a pendant, poly(2-phenyl-1,3-dithiolane) (PPDT), poly(1,4-di(1,3-dithiolan-2-yl)benzene) (PDDTB), poly(tetrahydrobenzodithiophene) (PTHBDT), poly[1,2,4,5-tetrakis(propylthio)benzene] (PTKPTB, or poly[3,4(ethylenedithio)thiophene] (PEDTT).

In other embodiments, the cathode active material layer contains an organic material selected from a phthalocyanine compound, such as copper phthalocyanine, zinc phthalocyanine, tin phthalocyanine, iron phthalocyanine, lead phthalocyanine, nickel phthalocyanine, vanadyl phthalocyanine, fluorochromium phthalocyanine, magnesium phthalocyanine, manganous phthalocyanine, dilithium phthalocyanine, aluminum phthalocyanine chloride, cadmium phthalocyanine, chlorogallium phthalocyanine, cobalt phthalocyanine, silver phthalocyanine, a metal-free phthalocyanine, a chemical derivative thereof, or a combination thereof.

The cathode active material is preferably in a form of nanoparticle (spherical, ellipsoidal, and irregular shape), nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a thickness or diameter less than 100 nm. These shapes can be collectively referred to as “particles” unless otherwise specified or unless a specific type among the above species is desired. Further preferably, the cathode active material has a dimension less than 50 nm, even more preferably less than 20 nm, and most preferably less than 10 nm. In some embodiments, one particle or a cluster of particles may be coated with or embraced by a layer of carbon disposed between the particle(s) and/or a sulfonated elastomer composite layer (an encapsulating shell).

The cathode layer may further contain a graphite, graphene, or carbon material mixed with the cathode active material particles. The carbon or graphite material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, mesophase pitch, carbon black, coke, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, or a combination thereof. Graphene may be selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, hydrogenated graphene, nitrogenated graphene, functionalized graphene, etc.

The cathode active material particles may be coated with or embraced by a conductive protective coating, selected from a carbon material, graphene, electronically conductive polymer, conductive metal oxide, or conductive metal coating. Preferably, the cathode active material, in the form of a nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn is pre-intercalated or pre-doped with lithium ions to form a prelithiated anode active material having an amount of lithium from 0.1% to 54.7% by weight of said prelithiated anode active material.

The present invention also provides a lithium metal-air battery comprising an air cathode, an anode comprising a sulfonated elastomer composite based protective layer as defined above, and electrolyte, or electrolyte combined with a separator, disposed between the anode and the air cathode. In the air cathode, oxygen from the open air (or from an oxygen supplier external to the battery) is the primary cathode active material. The air cathode needs an inert material to support the lithium oxide material formed at the cathode. The applicants have surprisingly found that an integrated structure of conductive nanofilaments can be used as an air cathode intended for supporting the discharge product (e.g., lithium oxide).

Hence, a further embodiment of the present invention is a lithium metal-air battery, wherein the air cathode comprises an integrated structure of electrically conductive nanometer-scaled filaments that are interconnected to form a porous network of electron-conducting paths comprising interconnected pores, wherein the filaments have a transverse dimension less than 500 nm (preferably less than 100 nm). These nanofilaments can be selected from carbon nanotubes (CNTs), carbon nanofibers (CNFs), graphene sheets, carbon fibers, graphite fibers, etc.

The invention also provides a method of manufacturing a lithium battery, the method comprising: (a) providing a cathode active material layer and an optional cathode current collector to support the cathode active material layer; (b) providing an anode active material layer (containing a lithium metal or lithium alloy foil or coating) and an optional anode current collector to support the lithium metal or lithium alloy foil or coating; (c) providing an electrolyte in contact with the anode active material layer and the cathode active material layer and an optional separator electrically separating the anode and the cathode; and (d) providing an anode-protecting layer of a sulfonated elastomer composite having a recoverable tensile elastic strain from 2% to 800% (preferably from 5% to 300%), a lithium ion conductivity no less than 10⁻⁶ S/cm at room temperature, and a thickness from 1 nm to 100 m (preferably from 10 nm to 10 m). This anode-protecting layer is disposed between the lithium metal or lithium alloy foil or coating and the porous separator (or solid-state electrolyte).

The invention also provides a method of improving the cycle-life of a lithium metal secondary battery (not including a lithium-sulfur battery or lithium-selenium battery). The method comprises implementing an anode-protecting layer between an anode active material layer and a porous separator/electrolyte, wherein the anode-protecting layer comprises a conductive sulfonated elastomer composite having from 0.01% to 50% by weight of a conductive reinforcement material dispersed in a sulfonated elastomeric matrix material and the layer of conductive sulfonated elastomer composite has a thickness from 1 nm to 100 μm, a fully recoverable tensile strain from 2% to 500%, a lithium ion conductivity from 10⁻⁷ S/cm to 5×10⁻² S/cm, and an electrical conductivity from 10⁻⁷ S/cm to 100 S/cm when measured at room temperature. Basically, this protecting layer is both electron-conducting and lithium ion-conducting.

In some embodiments, the conductive reinforcement material used in the method is selected from graphene sheets, carbon nanotubes, carbon nanofibers, carbon or graphite fibers, expanded graphite flakes, metal nanowires, conductive polymer fibers, or a combination thereof.

In some embodiments, the sulfonated elastomeric matrix material contains a material selected from a sulfonated version of natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, metallocene-based poly(ethylene-co-octene) elastomer, poly(ethylene-co-butene) elastomer, styrene-ethylene-butadiene-styrene elastomer, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof.

In the above-defined method, the step of implementing an anode-protecting layer is conducted by depositing a layer of a sulfonated elastomer composite onto one primary surface of the anode active material layer to form a protected anode, optionally compressing the protected anode to improve a contact between the anode-protecting layer and the anode active material layer, followed by combining the protected anode, the separator/electrolyte, and the cathode together to form the lithium metal secondary battery. A good contact between the anode active material layer and the anode-protecting layer is essential.

In certain embodiments, the step of implementing an anode-protecting layer is conducted by depositing a layer of first sulfonated elastomer composite onto one primary surface of the separator to form a coated separator, followed by combining the anode, the coated separator, the cathode, and the electrolyte together to form the lithium metal secondary battery. A compressive stress may be advantageously applied (e.g. via press-rolling) to improve the contact between the anode-protecting layer and the anode active material layer to be protected.

In certain embodiments, the step of implementing an anode-protecting layer is conducted by forming a layer of a sulfonated elastomer composite, followed by laminating the anode layer, the layer of sulfonated elastomer composite, the separator layer, the cathode layer, along with the electrolyte to form the lithium metal secondary battery, wherein an optional (but desirable) compressive stress is applied to improve the contact between the anode-protecting layer and the anode active material layer during or after this laminating step.

Preferably, the sulfonated elastomer composite has a lithium-ion conductivity from 10⁻⁵ S/cm to 5×10⁻² S/cm. In some embodiments, the sulfonated elastomer composite has a recoverable tensile strain from 10% to 300% (more preferably >30%, and further more preferably >50%).

In certain embodiments, the procedure of providing a sulfonated elastomer composite contains providing a mixture/blend/composite of a sulfonated elastomer with an electronically conductive polymer (e.g. polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof), a lithium-ion conducting material, a reinforcement material (e.g. carbon nanotube, carbon nanofiber, and/or graphene), or a combination thereof.

In this mixture/blend/composite, the lithium ion-conducting material is dispersed in the sulfonated elastomer composite and is preferably selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x<1 and 1<y<4.

In some embodiments, the lithium ion-conducting material is dispersed in the sulfonated elastomer composite and is selected from lithium perchlorate (LiClO₄), lithium hexafluoro-phosphate (LiPF₆), lithium borofluoride (LiBF₄), lithium hexafluoroarsenide (LiAsF₆), lithium trifluoro-methanesulfonate (LiCF₃SO₃), bis-trifluoromethyl sulfonylimide lithium (LiN(CF₃SO₂)₂), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF₂C₂O₄), lithium nitrate (LiNO₃), Li-fluoroalkyl-phosphates (LiPF₃(CF₂CF₃)₃), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.

The anode-protecting layer implemented between the anode active layer and the separator (or the solid-state electrolyte) is mainly for the purpose of reducing or eliminating the lithium metal dendrite by providing a more stable Li metal-electrolyte interface that is more conducive to uniform deposition of Li metal during battery charges. This anode-protecting layer also acts to block the penetration of any dendrite, if initiated, from reaching the separator or cathode. This anode-protecting layer, being highly elastic, also can shrink or expand responsive to the thickness increase or decrease of the anode active material layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 Schematic of a prior art lithium metal battery cell, containing an anode layer (a thin Li foil or Li coating deposited on a surface of a current collector, Cu foil), a porous separator, and a cathode active material layer, which is composed of particles of a cathode active material, a conductive additive (not shown) and a resin binder (not shown). A cathode current collector supporting the cathode active layer is also shown.

FIG. 2 Schematic of a presently invented lithium metal battery cell containing an anode layer (a thin Li foil or Li coating deposited on a surface of a current collector, Cu foil), a sulfonated elastomer composite-based anode-protecting layer, a porous separator/electrolyte layer (or a layer of solid-state electrolyte), and a cathode active material layer, which is composed of particles of a cathode active material, a conductive additive (not shown) and a resin binder (not shown). A cathode current collector supporting the cathode active layer is also shown.

FIG. 3 The specific intercalation capacity curves of four lithium cells: 2 cells each having a cathode containing V₂O₅ particles (one cell having an anode-protecting layer and the other not) and 2 cells each having a cathode containing graphene-embraced V₂O₅ particles (one cell having a rotaxane polymer-based protective layer and the other not).

FIG. 4 The specific capacity values of two lithium-LiCoO₂ cells (initially the cell being lithium-free) featuring (1) high-elasticity sulfonated elastomer composite layer at the anode and (2) no protection layer at the anode, respectively.

FIG. 5 The discharge capacity curves of two coin cells having a FeF₃-based of cathode active materials: (1) having a high-elasticity sulfonated elastomer composite-protected anode; and (2) no anode-protecting layer.

FIG. 6 Specific capacities of two lithium-FePc (organic) cells, each having Li foil as an anode active material and FePc/RGO mixture particles as the cathode active material (one cell containing a sulfonated elastomer composite-protected anode and the other no anode protection layer).

DESCRIPTION OF THE PREFERRED EMBODIMENTS

This invention is directed at a lithium metal secondary battery, which is preferably based on an organic electrolyte, a polymer gel electrolyte, an ionic liquid electrolyte, a quasi-solid electrolyte, or a solid-state electrolyte. The shape of a lithium metal secondary battery can be cylindrical, square, button-like, etc. The present invention is not limited to any battery shape or configuration or any type of electrolyte. The invented lithium secondary battery does not include a lithium-sulfur cell or lithium-selenium cell.

The invention provides a lithium metal secondary battery, comprising a cathode, an anode, and electrolyte (e.g. solid-state electrolyte) or separator-electrolyte assembly (porous separator and liquid electrolyte, gel electrolyte, quasi-solid electrolyte, etc.) disposed between the cathode and the anode, wherein the anode comprises: (a) a lithium metal (e.g. particles, foil or coating of lithium or lithium alloy) as an anode active material; and (b) a thin layer of a conductive sulfonated elastomer composite (anode-protecting layer) having from 0.01% to 50% by weight of a conductive reinforcement material dispersed in a sulfonated elastomeric matrix material and this layer of conductive sulfonated elastomer composite has a thickness from 1 nm to 100 μm, a fully recoverable tensile strain from 2% to 500%, a lithium ion conductivity from 10⁻⁷ S/cm to 5×10⁻² S/cm, and an electrical conductivity from 10⁻⁷ S/cm to 100 S/cm when measured at room temperature, wherein the sulfonated elastomer composite is disposed (interposed) between the lithium metal and the porous separator (or solid-state electrolyte. The foil or coating of lithium or lithium alloy may be supported by a current collector (e.g. a Cu foil, a Ni foam, a porous layer of nanofilaments, such as graphene sheets, carbon nanofibers, carbon nanotubes, etc. forming a 3D interconnected network of electron-conducting pathways).

Preferably, the sulfonated elastomer composite layer has a lithium ion conductivity no less than 10⁻⁶ S/cm (typically from 10⁻⁵ S/cm to 5 x10⁻² S/cm, measured at room temperature), and a thickness from 10 nm to 20 m.

In some embodiments, the sulfonated elastomer composite has from 0.01% to 50% by weight (based on the total weight of the sulfonated elastomer composite) of a conductive reinforcement material dispersed in a sulfonated elastomeric matrix material, wherein the conductive reinforcement material is selected from graphene sheets, carbon nanotubes, carbon nanofibers, metal nanowires, conductive polymer fibers, or a combination thereof.

The conducting reinforcement material is preferably in a filamentary or sheet-like form, such as a nanotube, nanofiber, nanowire, nanoplatelet, or nanodisc. In some embodiments, the conductive reinforcement material is selected from graphene sheets, carbon nanotubes, carbon nanofibers, carbon or graphite fibers, expanded graphite flakes, metal nanowires, conductive polymer fibers, or a combination thereof. These are electron-conducting materials and the sulfonated elastomer matrix is a lithium ion- and sodium ion-conducting material. By combining such a sulfonated elastomer and a conducting reinforcement (0-50% by weight, preferably 0.1%-30%, and more preferably 0.1-15%), one obtains a composite that is both electron conducting and ion-conducting and capable of allowing electrons and lithium ions to migrate in and out of the particulate without much resistance.

The graphene sheets to be dispersed in a sulfonated elastomer matrix are preferably selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, nitrogenated graphene, hydrogenated graphene, doped graphene, functionalized graphene, or a combination thereof. The graphene sheets preferably comprise single-layer graphene or few-layer graphene, wherein the few-layer graphene is defined as a graphene platelet formed of less than 10 graphene planes. The carbon nanotubes (CNTs) can be a single-walled CNT or multi-walled CNT. The carbon nanofibers may be vapor-grown carbon nanofibers or electrospinning based carbon nanofibers (e.g. electrospun polymer nanofibers that are subsequently carbonized).

Preferably, the sulfonated elastomeric matrix material contains a sulfonated version of an elastomer selected from natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, metallocene-based poly(ethyl ene-co-octene) (POE) elastomer, poly(ethylene-co-butene) (PBE) elastomer, styrene-ethylene-butadiene-styrene (SEBS) elastomer, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof.

Preferably, this anode-protecting layer is different in composition than the electrolyte per se used in the lithium battery and maintains as a discrete layer (not to be dissolved in the electrolyte) that is disposed between the anode active material layer (e.g. Li foil or Li coating on a current collector) and the electrolyte (or electrolyte-separator layer). The anode-protecting layer may contain a liquid electrolyte that permeates or impregnates into the sulfonated elastomer composite.

We have discovered that this protective layer provides several unexpected benefits: (a) the formation of dendrite has been essentially eliminated; (b) uniform deposition of lithium back to the anode side is readily achieved; (c) the layer ensures smooth and uninterrupted transport of lithium ions from/to the lithium foil/coating and through the interface between the lithium foil/coating and the protective layer with minimal interfacial resistance; and (d) cycle stability can be significantly improved and cycle life increased.

In a conventional lithium metal cell, as illustrated in FIG. 1, the anode active material (lithium) is deposited in a thin film form or a thin foil form directly onto an anode current collector (e.g. a Cu foil). The battery is a lithium metal battery, lithium sulfur battery, lithium-air battery, lithium-selenium battery, etc. As previously discussed in the Background section, these lithium secondary batteries have the dendrite-induced internal shorting and “dead lithium” issues at the anode.

We have solved these challenging issues that have troubled battery designers and electrochemists alike for more than 30 years by developing and implementing a new anode-protecting layer disposed between the lithium foil/coating and the separator layer. This protective layer comprises a sulfonated elastomer composite having a recoverable (elastic) tensile strain no less than 2% (preferably no less than 5%) under uniaxial tension and a lithium ion conductivity no less than 10⁻⁶ S/cm at room temperature (preferably and more typically from 1×10⁻⁵ S/cm to 5×10⁻² S/cm). The sulfonated elastomer composite contains a sulfonated elastomer composite network having a rotaxane structure or a sulfonated elastomer composite structure at a crosslink point of said sulfonated elastomer composite network.

As schematically shown in FIG. 2, one embodiment of the present invention is a lithium metal battery cell containing an anode layer (a thin Li foil or Li coating deposited on a surface of a current collector, Cu foil), a sulfonated elastomer composite-based anode-protecting layer, a porous separator, and a cathode active material layer, which is composed of particles of a cathode active material, a conductive additive (not shown) and a resin binder (not shown). A cathode current collector (e.g. Al foil) supporting the cathode active layer is also shown in FIG. 2. The lithium metal or alloy in the anode may be in a form of particles (e.g. surface-protected or surface-stabilized particles of Li or Li alloy).

Sulfonated elastomer composite exhibits an elastic deformation of at least 2% when measured under uniaxial tension. In the field of materials science and engineering, the “elastic deformation” is defined as a deformation of a material (when being mechanically stressed) that is essentially fully recoverable upon release of the load and the recovery is essentially instantaneous. The elastic deformation is preferably greater than 5%, more preferably greater than 10%, further more preferably greater than 30%, and still more preferably greater than 100% but less than 500%.

It may be noted that although FIG. 2 shows a lithium coating preexisting at the anode when the lithium battery is made, this is but one embodiment of the instant invention. An alternative embodiment is a lithium battery that does not contain a lithium foil or lithium coating at the anode (only an anode current collector, such as a Cu foil or a graphene/CNT mat) when the battery is made. The needed lithium to be bounced back and forth between the anode and the cathode is initially stored in the cathode active material (e.g. lithium vanadium oxide Li_(x)V₂O₅, instead of vanadium oxide, V₂O₅; or lithium transition metal oxide or phosphate, instead of, say, MoS₂). During the first charging procedure of the lithium battery (e.g. as part of the electrochemical formation process), lithium comes out of the cathode active material, migrates to the anode side, and deposits on the anode current collector. The presence of the presently invented sulfonated elastomer composite layer enables uniform deposition of lithium ions on the anode current collector surface. Such an alternative battery configuration avoids the need to have a layer of lithium foil or coating being present during battery fabrication. Bare lithium metal is highly sensitive to air moisture and oxygen and, thus, is more challenging to handle in a real battery manufacturing environment. This strategy of pre-storing lithium in the lithiated (lithium-containing) cathode active materials, such as Li_(x)V₂O₅ and Li₂S_(x), makes all the materials safe to handle in a real manufacturing environment. Cathode active materials, such as Li_(x)V₂O₅ and Li₂S_(x), are typically less air-sensitive.

The presently invented lithium secondary batteries can contain a wide variety of cathode active materials. The cathode active material layer may contain a cathode active material selected from an inorganic material, an organic material, a polymeric material, or a combination thereof. The inorganic material may be selected from a metal oxide, metal phosphate, metal silicide, metal selenide, transition metal sulfide, or a combination thereof.

The inorganic material may be selected from a lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, or a combination thereof.

In certain preferred embodiments, the inorganic material is selected from a metal fluoride or metal chloride including the group consisting of CoF₃, MnF₃, FeF₃, VF₃, VOF₃, TiF₃, BiF₃, NiF₂, FeF₂, CuF₂, CuF, SnF₂, AgF, CuCl₂, FeCl₃, MnCl₂, and combinations thereof. In certain preferred embodiments, the inorganic material is selected from a lithium transition metal silicate, denoted as Li₂MSiO₄ or Li₂Ma_(x)Mb_(y)SiO₄, wherein M and Ma are selected from Fe, Mn, Co, Ni, V, or VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; and x+y<1.

In certain preferred embodiments, the inorganic material is selected from a transition metal dichalcogenide, a transition metal trichalcogenide, or a combination thereof. The inorganic material is selected from TiS₂, TaS₂, MoS₂, NbSe₃, MnO₂, CoO₂, an iron oxide, a vanadium oxide, or a combination thereof.

The cathode active material layer may contain a metal oxide containing vanadium oxide selected from the group consisting of VO₂, Li_(x)VO₂, V₂O₅, Li_(x)V₂O₅, V₃O₈, Li_(x)V₃O₈, Li_(x)V₃O₇, V₄O₉, Li_(x)V₄O₉, V₆O₁₃, Li_(x)V₆O₁₃, their doped versions, their derivatives, and combinations thereof, wherein 0.1<x<5.

The cathode active material layer may contain a metal oxide or metal phosphate, selected from a layered compound LiMO₂, spinel compound LiM₂O₄, olivine compound LiMPO₄, silicate compound Li₂MSiO₄, tavorite compound LiMPO₄F, borate compound LiMBO₃, or a combination thereof, wherein M is a transition metal or a mixture of multiple transition metals.

In some embodiments, the inorganic material is selected from: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, manganese, iron, nickel, or a transition metal; (d) boron nitride, or (e) a combination thereof.

The cathode active material layer may contain an organic material or polymeric material selected from poly(anthraquinonyl sulfide) (PAQS), a lithium oxocarbon, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA), poly(anthraquinonyl sulfide), pyrene-4,5,9,10-tetraone (PYT), polymer-bound PYT, Quino(triazene), redox-active organic material, Tetracyanoquinodimethane (TCNQ), tetracyanoethylene (TCNE), 2,3,6,7,10,11-hexamethoxytriphenylene (HMTP), poly(5-amino-1,4-dyhydroxy anthraquinone) (PADAQ), phosphazene disulfide polymer ([(NPS₂)₃]n), lithiated 1,4,5,8-naphthalenetetraol formaldehyde polymer, hexaazatrinaphtylene (HATN), hexaazatriphenylene hexacarbonitrile (HAT(CN)₆), 5-benzylidene hydantoin, isatine lithium salt, pyromellitic diimide lithium salt, tetrahydroxy-p-benzoquinone derivatives (THQLi₄), N,N′-diphenyl-2,3,5,6-tetraketopiperazine (PHP), N,N′-diallyl-2,3,5,6-tetraketopiperazine (AP), N,N′-dipropyl-2,3,5,6-tetraketopiperazine (PRP), a thioether polymer, a quinone compound, 1,4-benzoquinone, 5,7,12,14-pentacenetetrone (PT), 5-amino-2,3-dihydro-1,4-dyhydroxy anthraquinone (ADDAQ), 5-amino-1,4-dyhydroxy anthraquinone (ADAQ), calixquinone, Li₄C₆O₆, Li₂C₆O₆, Li₆C₆O₆, or a combination thereof.

The thioether polymer is selected from poly[methanetetryl-tetra(thiomethylene)](PMTTM), poly(2,4-dithiopentanylene) (PDTP), a polymer containing poly(ethene-1,1,2,2-tetrathiol) (PETT) as a main-chain thioether polymers, a side-chain thioether polymer having a main-chain consisting of conjugating aromatic moieties, and having a thioether side chain as a pendant, poly(2-phenyl-1,3-dithiolane) (PPDT), poly(1,4-di(1,3-dithiolan-2-yl)benzene) (PDDTB), poly(tetrahydrobenzodithiophene) (PTHBDT), poly[1,2,4,5-tetrakis(propylthio)benzene] (PTKPTB, or poly[3,4(ethylenedithio)thiophene] (PEDTT).

In other embodiments, the cathode active material layer contains an organic material selected from a phthalocyanine compound, such as copper phthalocyanine, zinc phthalocyanine, tin phthalocyanine, iron phthalocyanine, lead phthalocyanine, nickel phthalocyanine, vanadyl phthalocyanine, fluorochromium phthalocyanine, magnesium phthalocyanine, manganous phthalocyanine, dilithium phthalocyanine, aluminum phthalocyanine chloride, cadmium phthalocyanine, chlorogallium phthalocyanine, cobalt phthalocyanine, silver phthalocyanine, a metal-free phthalocyanine, a chemical derivative thereof, or a combination thereof.

Preferably and typically, the sulfonated elastomer composite has a lithium ion conductivity no less than 10⁻⁵ S/cm, more preferably no less than 10⁻⁴ S/cm, further preferably no less than 10⁻³ S/cm, and most preferably no less than 10⁻² S/cm. In some embodiments, the sulfonated elastomer composite comprises from 0.1% to 50% (preferably 1% to 35%) by weight of a lithium ion-conducting additive dispersed in a sulfonated elastomer composite matrix material. The sulfonated elastomer composite must have a high elasticity (elastic deformation strain value >2%). An elastic deformation is a deformation that is fully recoverable and the recovery process is essentially instantaneous (no significant time delay). The sulfonated elastomer composite can exhibit an elastic deformation from 2% up to 800% (8 times of its original length), more typically from 5% to 500%, and further more typically from 10% to 300%, and most typically and desirably from 30% to 300%. It may be noted that although a metal typically has a high ductility (i.e. can be extended to a large extent without breakage), the majority of the deformation is plastic deformation (non-recoverable) and only a small amount of elastic deformation (typically <1% and more typically <0.2%).

Further, we have unexpectedly discovered that the presence of an amount of a lithium salt or sodium salt (1-35% by weight) and a liquid solvent (0-50%) can significantly increase the lithium-ion or sodium ion conductivity.

Typically, a sulfonated elastomer composite is originally in a monomer or oligomer states that can be cured to form a cross-linked polymer that is highly elastic. Prior to curing, these polymers or oligomers are soluble in an organic solvent to form a polymer solution. An ion-conducting or electron-conducting additive may be added to this solution to form a suspension.

This solution or suspension can then be formed into a thin layer of polymer precursor on a surface of an anode current collector. The polymer precursor (monomer or oligomer and initiator) is then polymerized and cured to form a lightly cross-linked polymer. This thin layer of polymer may be tentatively deposited on a solid substrate (e.g. surface of a polymer or glass), dried, and separated from the substrate to become a free-standing polymer layer. This free-standing layer is then laid on a lithium foil/coating or implemented between a lithium film/coating and electrolyte or separator. Polymer layer formation can be accomplished by using one of several procedures well-known in the art; e.g. spraying, spray-painting, printing, coating, extrusion-based film-forming, casting, etc.

One may dispense and deposit a layer of a sulfonated elastomer composite onto a primary surface of the anode active material layer. Alternatively, one may dispense and deposit a layer of a sulfonated elastomer composite onto a primary surface of a separator layer. Further alternatively, one may prepare separate free-standing discrete layers of the sulfonated elastomer composite first. This sulfonated elastomer composite layer is then laminated together with the anode active material layer, separator/electrolyte, and the cathode layer to form a battery cell.

Sulfonation of an elastomer or rubber may be accomplished by exposing the elastomer/rubber to a sulfonation agent in a solution state or melt state, in a batch manner or in a continuous process. The sulfonating agent may be selected from sulfuric acid, sulfonic acid, sulfur trioxide, chlorosulfonic acid, a bisulfate, a sulfate (e.g. zinc sulfate, acetyl sulfate, etc.), a mixture thereof, or a mixture thereof with another chemical species (e.g. acetic anhydride, thiolacetic acid, or other types of acids, etc.). In addition to zinc sulfate, there are a wide variety of metal sulfates that may be used as a sulfonating agent; e.g. those sulfates containing Mg, Ca, Co, Li, Ba, Na, Pb, Ni, Fe, Mn, K, Hg, Cr, and other transition metals, etc.

For instance, a triblock copolymer, poly(styrene-isobutylene-styrene) or SIBS, may be sulfonated to several different levels ranging from 0.36 to 2.04 mequiv./g (13 to 82 mol % of styrene; styrene being 19 mol % of the unsulfonated block copolymer). Sulfonation of SIBS may be performed in solution with acetyl sulfate as the sulfonating agent. First, acetic anhydride reacts with sulfuric acid to form acetyl sulfate (a sulfonating agent) and acetic acid (a by-product). Then, excess water is removed since anhydrous conditions are required for sulfonation of SIBS. The SIBS is then mixed with the mixture of acetyl sulfate and acetic acid. Such a sulfonation reaction produces sulfonic acid substituted to the para-position of the aromatic ring in the styrene block of the polymer. Elastomers having an aromatic ring may be sulfonated in a similar manner.

A sulfonated elastomer also may be synthesized by copolymerization of a low level of functionalized (i.e. sulfonated) monomer with an unsaturated monomer (e.g. olefinic monomer, isoprene monomer or oligomer, butadiene monomer or oligomer, etc.).

A broad array of elastomers can be sulfonated to become sulfonated elastomers. The elastomeric material may be selected from natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.

In some embodiments, a sulfonated elastomer composite can form a polymer matrix composite containing a lithium ion-conducting additive dispersed in the sulfonated elastomer composite matrix material, wherein the lithium ion-conducting additive is selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x<1, 1<y<4.

In some embodiments, the sulfonated elastomer composite can be mixed with a lithium ion-conducting additive, which contains a lithium salt selected from lithium perchlorate (LiClO₄), lithium hexafluorophosphate (LiPF₆), lithium borofluoride (LiBF₄), lithium hexafluoroarsenide (LiAsF₆), lithium trifluoro-methanesulfonate (LiCF₃SO₃), bis-trifluoromethyl sulfonylimide lithium (LiN(CF₃SO₂)₂), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF₂C₂O₄), lithium nitrate (LiNO₃), Li-fluoroalkyl-phosphates (LiPF₃(CF₂CF₃)₃), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.

The sulfonated elastomer composite may form a mixture, blend, or interpenetrating network with an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof. In some embodiments, the sulfonated elastomer composite may form a mixture, co-polymer, or semi-interpenetrating network with a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a derivative thereof (e.g. sulfonated versions), or a combination thereof.

The electrolyte for a lithium secondary cell may be an organic electrolyte, ionic liquid electrolyte, gel polymer electrolyte, solid-state electrolyte (e.g. polymer solid electrolyte or inorganic solid electrolyte), quasi-solid electrolyte or a combination thereof. The electrolyte typically contains an alkali metal salt (lithium salt, sodium salt, and/or potassium salt) dissolved in a solvent.

The solvent may be selected from 1,3-dioxolane (DOL), 1,2-dimethoxyethane (DME), tetraethylene glycol dimethylether (TEGDME), poly(ethylene glycol) dimethyl ether (PEGDME), diethylene glycol dibutyl ether (DEGDBE), 2-ethoxyethyl ether (EEE), sulfone, sulfolane, ethylene carbonate (EC), dimethyl carbonate (DMC), methylethyl carbonate (MEC), diethyl carbonate (DEC), ethyl propionate, methyl propionate, propylene carbonate (PC), gamma-butyrolactone (y-BL), acetonitrile (AN), ethyl acetate (EA), propyl formate (PF), methyl formate (MF), toluene, xylene, methyl acetate (MA), fluoroethylene carbonate (FEC), vinylene carbonate (VC), allyl ethyl carbonate (AEC), a hydrofluoroether, a room temperature ionic liquid solvent, or a combination thereof.

The electrolytic salts to be incorporated into a non-aqueous electrolyte may be selected from a lithium salt such as lithium perchlorate (LiClO₄), lithium hexafluorophosphate (LiPF₆), lithium borofluoride (LiBF₄), lithium hexafluoroarsenide (LiAsF₆), lithium trifluoro-methanesulfonate (LiCF₃SO₃), bis-trifluoromethyl sulfonylimide lithium [LiN(CF₃SO₂)₂], lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF₂C₂O₄), lithium nitrate (LiNO₃), Li-fluoroalkyl-phosphates (LiPF3(CF₂CF₃)₃), lithium bisperfluoroethylsulfonylimide (LiBETI), an ionic liquid salt, sodium perchlorate (NaClO₄), potassium perchlorate (KClO₄), sodium hexafluorophosphate (NaPF₆), potassium hexafluorophosphate (KPF₆), sodium borofluoride (NaBF₄), potassium borofluoride (KBF₄), sodium hexafluoroarsenide, potassium hexafluoroarsenide, sodium trifluoro-methanesulfonate (NaCF₃SO₃), potassium trifluoro-methanesulfonate (KCF₃SO₃), bis-trifluoromethyl sulfonylimide sodium (NaN(CF₃SO₂)₂), sodium trifluoromethanesulfonimide (NaTFSI), and bis-trifluoromethyl sulfonylimide potassium (KN(CF₃SO₂)₂). Among them, LiPF₆, LiBF₄ and LiN(CF₃SO₂)₂ are preferred for Li—S cells, NaPF₆ and LiBF₄ for Na—S cells, and KBF₄ for K—S cells. The content of aforementioned electrolytic salts in the non-aqueous solvent is preferably 0.5 to 3.0 M (mol/L) at the cathode side and 3.0 to >10 M at the anode side.

The ionic liquid is composed of ions only. Ionic liquids are low melting temperature salts that are in a molten or liquid state when above a desired temperature. For instance, a salt is considered as an ionic liquid if its melting point is below 100° C. If the melting temperature is equal to or lower than room temperature (25° C.), the salt is referred to as a room temperature ionic liquid (RTIL). The IL salts are characterized by weak interactions, due to the combination of a large cation and a charge-delocalized anion. This results in a low tendency to crystallize due to flexibility (anion) and asymmetry (cation).

A typical and well-known ionic liquid is formed by the combination of a 1-ethyl-3-methylimidazolium (EMI) cation and an N,N-bis(trifluoromethane)sulphonamide (TFSI) anion. This combination gives a fluid with an ionic conductivity comparable to many organic electrolyte solutions and a low decomposition propensity and low vapor pressure up to ˜300-400° C. This implies a generally low volatility and non-flammability and, hence, a much safer electrolyte for batteries.

Ionic liquids are basically composed of organic ions that come in an essentially unlimited number of structural variations owing to the preparation ease of a large variety of their components. Thus, various kinds of salts can be used to design the ionic liquid that has the desired properties for a given application. These include, among others, imidazolium, pyrrolidinium and quaternary ammonium salts as cations and bis(trifluoromethanesulphonyl) imide, bis(fluorosulphonyl)imide, and hexafluorophosphate as anions. Based on their compositions, ionic liquids come in different classes that basically include aprotic, protic and zwitterionic types, each one suitable for a specific application.

Common cations of room temperature ionic liquids (RTILs) include, but not limited to, tetraalkylammonium, di-, tri-, and tetra-alkylimidazolium, alkylpyridinium, dialkyl-pyrrolidinium, dialkylpiperidinium, tetraalkylphosphonium, and trialkylsulfonium. Common anions of RTILs include, but not limited to, BF₄ ⁻, B(CN)₄ ⁻, CH₃BF₃ ⁻, CH2CHBF₃ ⁻, CF₃BF₃ ⁻, C₂F₅BF₃ ⁻, n-C₃F₇BF₃ ⁻, n-C₄F₉BF₃ ⁻, PF₆ ⁻, CF₃CO₂ ⁻, CF₃SO₃ ⁻, N(SO₂CF₃)₂ ⁻, N(COCF₃)(SO₂CF₃)⁻, N(SO₂F)₂ ⁻, N(CN)₂ ⁻, C(CN)₃ ⁻, SCN⁻, SeCN⁻, CuCl₂ ⁻, AlCl₄ ⁻, F(HF)_(2.3) ⁻, etc. Relatively speaking, the combination of imidazolium- or sulfonium-based cations and complex halide anions such as AlCl₄ ⁻, BF₄ ⁻, CF₃CO₂ ⁻, CF₃SO₃ ⁻, NTf₂ ⁻, N(SO₂F)₂ ⁻, or F(HF)_(2.3) ⁻ results in RTILs with good working conductivities.

RTILs can possess archetypical properties such as high intrinsic ionic conductivity, high thermal stability, low volatility, low (practically zero) vapor pressure, non-flammability, the ability to remain liquid at a wide range of temperatures above and below room temperature, high polarity, high viscosity, and wide electrochemical windows. These properties, except for the high viscosity, are desirable attributes when it comes to using an RTIL as an electrolyte ingredient (a salt and/or a solvent) in a lithium metal cell.

Example 1: Sulfonation of Triblock Copolymer Poly(Styrene-Isobutylene-Styrene) or SIBS

An example of the sulfonation procedure used in this study is summarized as follows: a 10% (w/v) solution of SIBS (50 g) and a desired amount of graphene oxide sheets (0.15% to 40.5% by wt.) in methylene chloride (500 ml) was prepared. The solution was stirred and refluxed at approximately 40 8 C, while a specified amount of acetyl sulfate in methylene chloride was slowly added to begin the sulfonation reaction. Acetyl sulfate in methylene chloride was prepared prior to this reaction by cooling 150 ml of methylene chloride in an ice bath for approximately 10 min. A specified amount of acetic anhydride and sulfuric acid was then added to the chilled methylene chloride under stirring conditions. Sulfuric acid was added approximately 10 min after the addition of acetic anhydride with acetic anhydride in excess of a 1:1 mole ratio. This solution was then allowed to return to room temperature before addition to the reaction vessel.

After approximately 5 h, the reaction was terminated by slowly adding 100 ml of methanol. The reacted polymer solution was then precipitated with deionized water. The precipitate was washed several times with water and methanol, separately, and then dried in a vacuum oven at 50° C. for 24 h. This washing and drying procedure was repeated until the pH of the wash water was neutral. After this process, the final polymer yield was approximately 98% on average. This sulfonation procedure was repeated with different amounts of acetyl sulfate to produce several sulfonated polymers with various levels of sulfonation or ion-exchange capacities (IECs). The mol % sulfonation is defined as: mol %=(moles of sulfonic acid/moles of styrene)×100%, and the IEC is defined as the mille-equivalents of sulfonic acid per gram of polymer (mequiv./g).

After sulfonation and washing of each polymer, the S-SIBS samples were dissolved in a mixed solvent of toluene/hexanol (85/15, w/w) with concentrations ranging from 0.5 to 2.5% (w/v). Desired amounts of graphene sheets (if not added at an earlier stage) were then added into the solution to form slurry samples. The slurry samples were slot-die coated into layers of sulfonated elastomer composite.

Example 2: Synthesis of Sulfonated Polybutadiene (PB) by Free Radical Addition of Thiolacetic Acid (TAA) Followed by In Situ Oxidation with Performic Acid

A representative procedure is given as follows. PB (8.0 g) was dissolved in toluene (800 mL) under vigorous stirring for 72 h at room temperature in a 1 L round-bottom flask. Benzophenone (BZP) (0.225 g; 1.23 mmol; BZP/olefin molar ratio=1:120) and TAA (11.9 mL; 0.163 mol, TAA/olefin molar ratio=1.1) and a desired amount of graphene sheets (0.1%-40% by wt.) were introduced into the reactor, and the polymer solution was irradiated for 1 h at room temperature with UV light of 365 nm and power of 100 W.

The resulting thioacetylated polybutadiene (PB-TA)/graphene composite was isolated by pouring 200 mL of the toluene solution in a plenty of methanol and the polymer recovered by filtration, washed with fresh methanol, and dried in vacuum at room temperature (Yield=3.54 g). Formic acid (117 mL; 3.06 mol; HCOOH/olefin molar ratio=25), along with a desired amount of anode active material particles, from 10 to 100 grams) were added to the toluene solution of PB-TA at 50° C. followed by slow addition of 52.6 mL of hydrogen peroxide (35 wt %; 0.61 mol; H₂O₂/olefin molar ratio=5) in 20 min. We would like to caution that the reaction is autocatalytic and strongly exothermic. The resulting slurry was spray-dried to obtain sulfonated polybutadiene (PB-SA)/graphene composite layers.

It may be noted that graphene sheets may be added at different stages of the procedure: before, during or after BZP is added or before/during/after the active material particles are added.

Example 3: Synthesis of Sulfonated SBS

Sulfonated styrene-butadiene-styrene triblock copolymer (SBS) based elastomer was directly synthesized. First, SBS (optionally along with graphene sheets) is first epoxidized by performic acid formed in situ, followed by ring-opening reaction with an aqueous solution of NaHSO₃. In a typical procedure, epoxidation of SBS was carried out via reaction of SBS in cyclohexane solution (SBS concentration=11 g/100 mL) with performic acid formed in situ from HCOOH and 30% aqueous H₂O₂ solution at 70° C. for 4 h, using 1 wt % poly(ethylene glycol)/SBS as a phase transfer catalyst. The molar ratio of H₂O₂/HCOOH was 1. The product (ESBS) was precipitated and washed several times with ethanol, followed by drying in a vacuum dryer at 60° C.

Subsequently, ESBS was first dissolved in toluene to form a solution with a concentration of 10 g/100 mL, into which was added 5 wt % TEAB/ESBS as a phase transfer catalyst and 5 wt % DMA/ESBS as a ring-opening catalyst. Herein, TEAB=tetraethyl ammonium bromide and DMA=N,N-dimethyl aniline. An aqueous solution of NaHSO₃ and Na₂SO₃ (optionally along with graphene sheets or CNTs, if not added earlier) was then added with vigorous stirring at 60° C. for 7 h at a molar ratio of NaHSO₃/epoxy group at 1.8 and a weight ratio of Na₂SO₃/NaHSO₃ at 36%. This reaction allows for opening of the epoxide ring and attaching of the sulfonate group according to the following reaction:

The reaction was terminated by adding a small amount of acetone solution containing antioxidant. The mixture was washed with distilled water and then precipitated by ethanol while being cast into thin films, followed by drying in a vacuum dryer at 50° C. It may be noted that graphene sheets (or CNTs, etc.) may be added during various stages of the aforementioned procedure (e.g. right from the beginning, or prior to the ring opening reaction).

Example 4: Synthesis of Sulfonated SBS by Free Radical Addition of Thiolacetic Acid (TAA) Followed by In Situ Oxidation with Per-Formic Acid

A representative procedure is given as follows. SBS (8.000 g) in toluene (800 mL) was left under vigorous stirring for 72 hours at room temperature and heated later on for 1 h at 65° C. in a 1 L round-bottom flask until the complete dissolution of the polymer. Thus, benzophenone (BZP, 0.173 g; 0.950 mmol; BZP/olefin molar ratio=1:132) and TAA (8.02 mL; 0.114 mol, TAA/olefin molar ratio=1.1) were added, and the polymer solution was irradiated for 4 h at room temperature with UV light of 365 nm and power of 100 W. To isolate a fraction of the thioacetylated sample (S(B-TA)S), 20 mL of the polymer solution was treated with plenty of methanol, and the polymer was recovered by filtration, washed with fresh methanol, and dried in vacuum at room temperature. The toluene solution containing the thioacetylated polymer was equilibrated at 50° C., and 107.4 mL of formic acid (2.84 mol; HCOOH/olefin molar ratio=27.5) and 48.9 mL of hydrogen peroxide (35 wt %; 0.57 mol; H₂O₂/olefin molar ratio=5.5) were added in about 15 min. It may be cautioned that the reaction is autocatalytic and strongly exothermic! The conductive reinforcement material was added before or after this reaction. The resulting slurry was stirred for 1 h, and then most of the solvent was distilled off in vacuum at 35° C. Finally, the slurry containing the sulfonated elastomer was added with acetonitrile, cast into films, washed with fresh acetonitrile, and dried in vacuum at 35° C. to obtain layers of sulfonated elastomers.

Other elastomers (e.g. polyisoprene, EPDM, EPR, polyurethane, etc.) were sulfonated in a similar manner. Alternatively, all the rubbers or elastomers can be directly immersed in a solution of sulfuric acid, a mixture of sulfuric acid and acetyl sulfate, or other sulfonating agent discussed above to produce sulfonated elastomers/rubbers. Again, graphene sheets (or other conductive reinforcement material) may be added at various stages of the procedure.

Example 5: Lithium Battery Containing a Sulfonated Elastomer Composite-Protected Lithium Anode and a Cathode Containing V₂O₅ Particles

Cathode active material layers were prepared from V₂O₅ particles and graphene-embraced V₂O₅ particles, respectively. The V₂O₅ particles were commercially available. Graphene-embraced V₂O₅ particles were prepared in-house. In a typical experiment, vanadium pentoxide gels were obtained by mixing V₂O₅ in a LiCl aqueous solution. The Li⁺-exchanged gels obtained by interaction with LiCl solution (the Li:V molar ratio was kept as 1:1) was mixed with a GO suspension and then placed in a Teflon-lined stainless steel 35 ml autoclave, sealed, and heated up to 180° C. for 12 h. After such a hydrothermal treatment, the green solids were collected, thoroughly washed, ultrasonicated for 2 minutes, and dried at 70° C. for 12 h followed by mixing with another 0.1% GO in water, ultrasonicating to break down nanobelt sizes, and then spray-drying at 200° C. to obtain graphene-embraced V₂O₅ composite particulates. Selected amounts of V₂O₅ particles and graphene-embraced V₂O₅ particles, respectively, were then each made into a cathode layer following a well-known slurry coating process.

The sulfonated elastomer composite films for anode protection were SIBS as prepared in Example 1. Several tensile testing specimens were cut from the film and tested with a universal testing machine. The results indicate that this series of sulfonated elastomer films have an elastic deformation from approximately 150% to 465%. The addition of up to 30% by weight of a conductive reinforcement material (CNTs, graphene, CNFs, etc.) typically reduces this elasticity down to a reversible tensile strain from 7% to 130%.

For electrochemical testing, the working electrodes (cathode layers) were prepared by mixing 85 wt. % V₂O₅ or 88% of graphene-embraced V₂O₅ particles, 5-8 wt. % CNTs, and 7 wt. % polyvinylidene fluoride (PVDF) binder dissolved in N-methyl-2-pyrrolidinoe (NMP) to form a slurry of 5 wt. % total solid content. After coating the slurries on Al foil, the electrodes were dried at 120° C. in vacuum for 2 h to remove the solvent before pressing. Then, the electrodes were cut into a disk (4=12 mm) and dried at 100° C. for 24 h in vacuum.

Electrochemical measurements were carried out using CR2032 (3V) coin-type cells with lithium metal as the counter electrode (actually an anode of a Li-transition metal oxide cell), Celgard 2400 membrane as separator, and 1 M LiPF₆ electrolyte solution dissolved in a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) (EC-DEC, 1:1 v/v). The cell assembly was performed in an argon-filled glove-box. The CV measurements were carried out using a CH-6 electrochemical workstation at a scanning rate of 1 mV/s. The electrochemical performance of the cell featuring sulfonated elastomer composite binder and that containing PVDF binder were evaluated by galvanostatic charge/discharge cycling at a current density of 50 mA/g using an Arbin electrochemical workstation.

Summarized in FIG. 3 are the specific intercalation capacity curves of four lithium cells: 2 cells each having a cathode containing V₂O₅ particles (one cell having a sulfonated elastomer composite-based lithium metal anode-protecting layer and the other not) and 2 cells each having a cathode containing graphene-embraced V₂O₅ particles (one cell having a sulfonated elastomer composite-based lithium anode-protecting layer and the other not). As the number of cycles increases, the specific capacity of the un-protected cells drops at the fastest rate. In contrast, the presently invented sulfonated elastomer composite protection layer provides the battery cell with a significantly more stable and high specific capacity for a large number of cycles. These data have clearly demonstrated the surprising and superior performance of the presently invented sulfonated elastomer composite protection approach.

The sulfonated elastomer composite protective layer appears to be capable of reversibly deforming to a great extent without breakage when the lithium foil decreases in thickness during battery discharge. The protective layer also prevents the continued reaction between liquid electrolyte and lithium metal at the anode, reducing the problem of continuing loss in lithium and electrolyte. This also enables a significantly more uniform deposition of lithium ions upon returning from the cathode during a battery re-charge step; hence, no lithium dendrite. These were observed by using SEM to examine the surfaces of the electrodes recovered from the battery cells after some numbers of charge-discharge cycles.

Example 6: Sulfonated Elastomer Composite Implemented in the Anode of a Lithium-LiCoO₂ Cell (Initially the Cell Anode has an Ultra-Thin Lithium Layer, <1 m Thick)

The sulfonated elastomer composite as a lithium-protecting layer was based on the sulfonated polybutadiene (PB) prepared according to a procedure used in Example 2. Tensile testing was also conducted on the sulfonated elastomer films (without the conductive reinforcement material). This series of sulfonated elastomers can be elastically stretched up to approximately 135% (having some lithium salt or conductive reinforcement material dispersed therein) or up to 770% (with no additive).

FIG. 4 shows that the cell having an anode-protecting polymer layer offers a significantly more stable cycling behavior. The sulfonated elastomer composite also acts to isolate the electrolyte from the lithium coating yet still allowing for easy diffusion of lithium ions.

Example 7: Li Metal Cells Containing Transition Metal Fluoride Nanoparticle-Based Cathode and a Sulfonated Elastomer Composite-Protected Lithium Anode

This sulfonated elastomer composite layers were based on sulfonated styrene-butadiene-styrene triblock copolymer (SBS). Tensile testing was conducted on some cut pieces of these layers. This series of cross-linked polymers can be elastically stretched up to approximately 820% (without any additive). The addition of additives results in an elasticity of approximately 5% (e.g. with 20% carbon black) to 160% (e.g. with 5% graphene sheets, as a conductive additive).

Commercially available powders of CoF₃, MnF₃, FeF₃, VF₃, VOF₃, TiF₃, and BiF₃ were subjected to high-intensity ball-milling to reduce the particle size down to approximately 0.5-2.3 m. Each type of these metal fluoride particles, along with graphene sheets (as a conductive additive), was then added into an NMP and PVDF binder suspension to form a multiple-component slurry. The slurry was then slurry-coated on Al foil to form cathode layers.

Shown in FIG. 5 are the discharge capacity curves of two coin cells having the same cathode active material (FeF₃), but one cell having a sulfonated elastomer composite-protected anode and the other having no protective layer. These results have clearly demonstrated that the sulfonated elastomer composite protection strategy provides excellent protection against capacity decay of a lithium metal battery.

The sulfonated elastomer composite appears to be capable of reversibly deforming without breakage when the anode layer expands and shrinks during charge and discharge. The polymer also prevents continued reaction between the liquid electrolyte and the lithium metal. No dendrite-like features were found with the anode being protected by a sulfonated elastomer composite. This was confirmed by using SEM to examine the surfaces of the electrodes recovered from the battery cells after some numbers of charge-discharge cycles.

Example 8: Li-Organic Cell Containing a Naphthalocyanine/Reduced Graphene Oxide (FePc/RGO) Particulate Cathode and a Protected Li Foil Anode

Particles of combined FePc/graphene sheets were obtained by ball-milling a mixture of FePc and RGO in a milling chamber for 30 minutes. The resulting FePc/RGO mixture particles were potato-like in shape. Two lithium cells were prepared, each containing a Li foil anode, a porous separator, and a cathode layer of FePc/RGO particles; one cell containing an anode-protecting layer and the other no protecting layer.

The cycling behaviors of these 2 lithium cells are shown in FIG. 6, which indicates that the lithium-organic cell having a sulfonated elastomer composite protection layer in the anode exhibits a significantly more stable cycling response. This protective layer reduces or eliminates the undesirable reactions between the lithium metal and the electrolyte, yet the sulfonated elastomer layer itself remains in ionic contact with the lithium metal and is permeable to lithium ions. This approach has significantly increased the cycle life of all lithium-organic batteries.

Example 9: Effect of Lithium Ion-Conducting Additive in a Sulfonated Elastomer Composite

A wide variety of lithium ion-conducting additives were added to several different polymer matrix materials to prepare anode protection layers. The lithium ion conductivity vales of the resulting complex materials are summarized in Table 1 below. We have discovered that these composite materials are suitable anode-protecting layer materials provided that their lithium ion conductivity at room temperature is no less than 10⁻⁶ S/cm. With these materials, lithium ions appear to be capable of readily diffusing through the protective layer having a thickness no greater than 1 μm. For thicker polymer films (e.g. 10 μm), a lithium ion conductivity at room temperature of these sulfonated elastomer composites no less than 10⁻⁴ S/cm would be required.

TABLE 1 Lithium ion conductivity of various sulfonated elastomer composite composite compositions as a lithium metal-protecting layer. Sample Lithium-conducting % sulfonated elastomer No. additive (1-2 μm thick) Li-ion conductivity (S/cm) E-1p Li₂CO₃ + (CH₂OCO₂Li)₂ 70-99% 1.3 × 10⁻⁴ to 3.3 × 10⁻³ S/cm B1p LiF + LiOH + Li₂C₂O₄ 60-90% 4.2 × 10⁻⁵ to 2.6 × 10⁻³ S/cm B2p LiF + HCOLi 80-99% 1.2 × 10⁻⁴ to 1.4 × 10⁻³ S/cm B3p LiOH 70-99% 8.5 × 10⁻⁴ to 1.1 × 10⁻² S/cm B4p Li₂CO₃ 70-99% 4.3 × 10⁻³ to 9.5 × 10⁻³ S/cm B5p Li₂C₂O₄ 70-99% 8.2 × 10⁻⁴ to 1.3 × 10⁻² S/cm B6p Li₂CO₃ + LiOH 70-99% 1.5 × 10⁻³ to 1.7 × 10⁻² S/cm C1p LiClO₄ 70-99% 4.0 × 10⁻⁴ to 2.2 × 10⁻³ S/cm C2p LiPF₆ 70-99% 2.1 × 10⁻⁴ to 6.2 × 10⁻³ S/cm C3p LiBF₄ 70-99% 1.2 × 10⁻⁴ to 1.7 × 10⁻³ S/cm C4p LiBOB + LiNO₃ 70-99% 1.4 × 10⁻⁴ to 3.2 × 10⁻³ S/cm S1p Sulfonated polyaniline 85-99% 3.2 × 10⁻⁵ to 9.5 × 10⁻⁴ S/cm S2p Sulfonated PEEK 85-99% 1.4 × 10⁻⁴ to 1.3 × 10⁻³ S/cm S3p Sulfonated PVDF 80-99% 1.7 × 10⁻⁴ to 1.5 × 10⁻⁴ S/cm S4p Polyethylene oxide 80-99% 4.2 × 10⁻⁴ to 3.4 × 103⁴ S/cm

Example 10: Cycle Stability of Various Rechargeable Lithium Battery Cells

In lithium-ion battery industry, it is a common practice to define the cycle life of a battery as the number of charge-discharge cycles that the battery suffers a 20% decay in capacity based on the initial capacity measured after the required electrochemical formation. Summarized in Table 2 below are the cycle life data of a broad array of batteries featuring an anode with or without an anode-protecting polymer layer.

TABLE 2 Cycle life data of various lithium secondary (rechargeable) batteries. Initial Cycle life Anode-protecting Type & % of cathode active capacity (No. of Sample ID polymer material (mAh/g) cycles) CuCl₂-1e sulfonated elastomer 85% by wt. CuCl₂ particles (80 536 1450 composite nm) + 7% graphite + 8% binder CuCl₂-2e none 85% by wt. CuCl₂ particles (80 536 115 nm) + 7% graphite + 8% binder BiF₃-1e none 85% by wt. BiFe₃ particles + 7% 275 115 graphene + 8% binder BiF₃-2e Sulfonated elastomer 85% by wt. BiFe₃ particles + 7% 276 1,446 composite + 50% graphene + 8% binder ethylene oxide Li₂MnSiO₄-1e sulfonated elastomer 85% C-coated Li₂MnSiO₄ + 7% 255 2,460 composite CNT + 8% binder Li₂MnSiO₄-2e none 85% C-coated Li₂MnSiO₄ + 7% 252 543 CNT+ 8% binder Li₆C₆O₆-1e sulfonated elastomer Li₆C₆O₆-graphene ball-milled 441 1,520 composite + 20% polyanniline Li₆C₆O₆-2e none Li₆C₆O₆-graphene ball-milled 438 116 MoS₂-1e sulfonated elastomer 85% MoS₂ + 8% graphite + 226 1,755 composite binder MoS₂-2e none 85% MoS₂ + 8% graphite + 225 156 binder

In conclusion, the sulfonated elastomer composite-based anode-protecting layer strategy is surprisingly effective in alleviating the problems of lithium metal dendrite formation and lithium metal-electrolyte reactions that otherwise lead to rapid capacity decay and potentially internal shorting and explosion of the lithium secondary batteries. The sulfonated elastomer composite is capable of expanding or shrinking congruently or conformably with the anode layer. This capability helps to maintain a good contact between the current collector (or the lithium film itself) and the protective layer, enabling uniform re-deposition of lithium ions without interruption.

The anode-protecting layer appears to be capable of performing at least the following three functions:

-   -   1) Being highly elastic, the sulfonated elastomer composite         layer helps to maintain a good contact between a Li metal layer         (e.g. lithium metal foil, as the anode active material) and an         electrolyte phase (e.g. an electrolyte/separator assembly or a         solid-state electrolyte phase) when the Li metal layer decreases         in thickness (e.g. due to dissolution of Li in the electrolyte         when the battery is discharged) or increases in thickness (e.g.         due to re-deposition of lithium metal back to the Cu foil or         lithium metal when the battery is recharged). The sulfonated         elastomer composite can expand and shrink responsive to the         shrinkage and expansion of the anode active material layer. Such         a conformal or congruent expansion/shrinkage of the sulfonated         elastomer composite helps to eliminate the potential gap between         the anode active material layer and the electrolyte or         separator, thereby maintaining the lithium ion migration paths         required of an operational Li metal battery.     -   2) The sulfonated elastomer matrix, infiltrated with a liquid         electrolyte (before, during, or after the cell is fabricated)         and coupled with its high-elasticity nature (good         electrode-electrolyte contact), enables the returning Li⁺ ions         to uniformly and successfully deposit back to the Li metal         surface or current collector surface, reducing the formation of         dead lithium particles, which otherwise become inactive. The         uniform deposition of Li metal also reduces the tendency to form         dangerous Li dendrites.     -   3) The presence of the conductive reinforcement material         (graphene sheets, CNTs, CNFs, etc.) are high-strength materials,         capable of stopping or deflecting the growth of dendrites (if         initiated), preventing the dendrite from penetrating the         separator to reach the cathode side to induce internal shorting,         which otherwise is a fire and explosion hazard. 

We claim:
 1. A lithium metal secondary battery comprising a cathode, an anode, and a porous separator or electrolyte disposed between said cathode and said anode, wherein said anode comprises: a) an anode active material layer containing a layer of lithium or lithium alloy, in a form of a foil, coating, or multiple particles aggregated together, as an anode active material; and b) an anode-protecting layer of a conductive sulfonated elastomer composite, disposed between said anode active material layer and said porous separator or electrolyte; wherein said conductive sulfonated elastomer composite has from 0.01% to 50% by weight of a conductive reinforcement material dispersed in a sulfonated elastomeric matrix material, a thickness from 1 nm to 100 μm, a fully recoverable tensile strain from 2% to 500%, a lithium ion conductivity from 10⁻⁷ S/cm to 5×10⁻² S/cm, and an electrical conductivity from 10⁻⁷ S/cm to 100 S/cm when measured at room temperature; wherein said lithium metal secondary battery does not include a lithium-sulfur battery or lithium-selenium battery.
 2. The lithium metal secondary battery of claim 1, wherein said conductive reinforcement material is selected from the group consisting of graphene sheets, carbon nanotubes, carbon nanofibers, carbon or graphite fibers, expanded graphite flakes, metal nanowires, conductive polymer fibers, and combinations thereof.
 3. The lithium metal secondary battery of claim 1, wherein said sulfonated elastomeric matrix material contains a material selected from the group consisting of a sulfonated version of natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, metallocene-based poly(ethylene-co-octene) elastomer, poly(ethylene-co-butene) elastomer, styrene-ethylene-butadiene-styrene elastomer, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.
 4. The lithium metal secondary battery of claim 2, wherein said graphene sheets are selected from the group consisting of pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, nitrogenated graphene, hydrogenated graphene, doped graphene, functionalized graphene, and combinations thereof.
 5. The lithium metal secondary battery of claim 2, wherein said graphene sheets comprise single-layer graphene or few-layer graphene, wherein said few-layer graphene is defined as a graphene platelet formed of less than 10 graphene planes.
 6. The lithium metal secondary battery of claim 2, wherein said graphene sheets have a length or width from 5 nm to 5 μm.
 7. The lithium metal secondary battery of claim 1, wherein said sulfonated elastomer composite further contains from 0.1% to 50% by weight of a lithium ion-conducting additive dispersed therein.
 8. The lithium metal secondary battery of claim 1, wherein said sulfonated elastomer composite contains a lithium ion-conducting additive dispersed therein and is selected from the group consisting of Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), and combinations thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1 and 1≤y≤4.
 9. The lithium metal secondary battery of claim 1, wherein said conductive reinforcement material is selected from the group consisting of an electron-conducting polymer, a metal particle or wire, a graphene sheet, a carbon fiber, a graphite fiber, a carbon nanofiber, a graphite nanofiber, a carbon nanotube, a graphite particle, an expanded graphite flake, an acetylene black particle, and combinations thereof.
 10. The lithium metal secondary battery of claim 9, wherein said conductive reinforcement material has a thickness or diameter less than 100 nm.
 11. The lithium metal secondary battery of claim 1, wherein said sulfonated elastomer composite further contains a lithium salt dispersed therein and said lithium salt is selected from the group consisting of lithium perchlorate (LiClO₄), lithium hexafluorophosphate (LiPF₆), lithium borofluoride (LiBF₄), lithium hexafluoroarsenide (LiAsF₆), lithium trifluoro-methanesulfonate (LiCF₃SO₃), bis-trifluoromethyl sulfonylimide lithium [LiN(CF₃SO₂)₂], lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF₂C₂O₄), lithium nitrate (LiNO₃), Li-fluoroalkyl-phosphates [LiPF₃(CF₂CF₃)₃], lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
 12. The lithium metal secondary battery of claim 1, wherein said sulfonated elastomer composite is mixed with an electron-conducting polymer selected from the group consisting of polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, and combinations thereof.
 13. The lithium metal secondary battery of claim 1, wherein the sulfonated elastomer composite forms a mixture or blend with a lithium ion-conducting polymer selected from the group consisting of poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a sulfonated derivative thereof, and combinations thereof.
 14. The lithium metal secondary battery of claim 1, wherein said anode-protecting layer has a thickness from 1 nm to 10 μm.
 15. The lithium metal secondary battery of claim 1, wherein said cathode active material is selected from the group consisting of an inorganic material, an organic material, a polymeric material, and combinations thereof, and said inorganic material does not include sulfur or alkali metal polysulfide.
 16. The lithium metal secondary battery of claim 15, wherein said inorganic material is selected from the group consisting of a metal oxide, metal phosphate, metal silicide, metal selenide, transition metal sulfide, and combinations thereof.
 17. The lithium metal secondary battery of claim 15, wherein said inorganic material is selected from the group consisting of a lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, and combinations thereof.
 18. The lithium metal secondary battery of claim 15, wherein said inorganic material is selected from the group consisting of a metal fluoride or metal chloride including the group consisting of CoF₃, MnF₃, FeF₃, VF₃, VOF₃, TiF₃, BiF₃, NiF₂, FeF₂, CuF₂, CuF, SnF₂, AgF, CuCl₂, FeCl₃, MnCl₂, and combinations thereof.
 19. The lithium metal secondary battery of claim 15, wherein said inorganic material is selected from a lithium transition metal silicate, denoted as Li₂MSiO₄ or Li₂Ma_(x)Mb_(y)SiO₄, wherein M and Ma are selected from the group consisting of Fe, Mn, Co, Ni, V, and VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; and x+y≤1.
 20. The lithium metal secondary battery of claim 15, wherein said inorganic material is selected from the group consisting of a transition metal dichalcogenide, a transition metal trichalcogenide, and combinations thereof.
 21. The lithium metal secondary battery of claim 15, wherein said inorganic material is selected from the group consisting of TiS₂, TaS₂, MoS₂, NbSe₃, MnO₂, COO₂, an iron oxide, a vanadium oxide, and combinations thereof.
 22. The lithium metal secondary battery of claim 16, wherein said metal oxide contains a vanadium oxide selected from the group consisting of VO₂, Li_(x)VO₂, V₂O₅, Li_(x)V₂O₅, V₃O₈, Li_(x)V₃O₈, Li_(x)V₃O₇, V₄O₉, Li_(x)V₄O₉, V₆O₁₃, Li_(x)V₆O₁₃, their doped versions, their derivatives, and combinations thereof, wherein 0.1<x<5.
 23. The lithium metal secondary battery of claim 16, wherein said metal oxide or metal phosphate is selected from the group consisting of a layered compound LiMO₂, spinel compound LiM₂O₄, olivine compound LiMPO₄, silicate compound Li₂MSiO₄, tavorite compound LiMPO₄F, borate compound LiMBO₃, and combinations thereof, wherein M is a transition metal or a mixture of multiple transition metals.
 24. The lithium metal secondary battery of claim 16, wherein said inorganic material is selected from the group consisting of (a) bismuth selenide or bismuth telluride; (b) transition metal dichalcogenide or trichalcogenide; (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, manganese, iron, nickel, or a transition metal; (d) boron nitride, and (e) combinations thereof.
 25. The lithium metal secondary battery of claim 15, wherein said organic material or polymeric material is selected from the group consisting of poly(anthraquinonyl sulfide) (PAQS), a lithium oxocarbon, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA), poly(anthraquinonyl sulfide), pyrene-4,5,9,10-tetraone (PYT), polymer-bound PYT, quino(triazene), redox-active organic material, tetracyanoquinodimethane (TCNQ), tetracyanoethylene (TCNE), 2,3,6,7,10,11-hexamethoxytriphenylene (HMTP), poly(5-amino-1,4-dyhydroxy anthraquinone) (PADAQ), phosphazene disulfide polymer ([(NPS₂)₃]n), lithiated 1,4,5,8-naphthalenetetraol formaldehyde polymer, hexaazatrinaphtylene (HATN), hexaazatriphenylene hexacarbonitrile (HAT(CN)₆), 5-benzylidene hydantoin, isatine lithium salt, pyromellitic diimide lithium salt, tetrahydroxy-p-benzoquinone derivatives (THQLi₄), N,N′-diphenyl-2,3,5,6-tetraketopiperazine (PHP), N,N′-diallyl-2,3,5,6-tetraketopiperazine (AP), N,N′-dipropyl-2,3,5,6-tetraketopiperazine (PRP), a thioether polymer, a quinone compound, 1,4-benzoquinone, 5,7,12,14-pentacenetetrone (PT), 5-amino-2,3-dihydro-1,4-dyhydroxy anthraquinone (ADDAQ), 5-amino-1,4-dyhydroxy anthraquinone (ADAQ), calixquinone, Li₄C₆O₆, Li₂C₆O₆, Li₆C₆O₆, and combinations thereof.
 26. The lithium metal secondary battery of claim 25, wherein said thioether polymer is selected from the group consisting of poly[methanetetryl-tetra(thiomethylene)] (PMTTM), poly(2,4-dithiopentanylene) (PDTP), a polymer containing poly(ethene-1,1,2,2-tetrathiol) (PETT) as a main-chain thioether polymers, a side-chain thioether polymer having a main-chain consisting of conjugating aromatic moieties, and having a thioether side chain as a pendant, poly(2-phenyl-1,3-dithiolane) (PPDT), poly(1,4-di(1,3-dithiolan-2-yl)benzene) (PDDTB), poly(tetrahydrobenzodithiophene) (PTHBDT), poly[1,2,4,5-tetrakis(propylthio)benzene](PTKPTB, poly[3,4(ethylenedithio)thiophene] (PEDTT), and combinations thereof.
 27. The lithium metal secondary battery of claim 15, wherein said organic material contains a phthalocyanine compound selected from the group consisting of copper phthalocyanine, zinc phthalocyanine, tin phthalocyanine, iron phthalocyanine, lead phthalocyanine, nickel phthalocyanine, vanadyl phthalocyanine, fluorochromium phthalocyanine, magnesium phthalocyanine, manganous phthalocyanine, dilithium phthalocyanine, aluminum phthalocyanine chloride, cadmium phthalocyanine, chlorogallium phthalocyanine, cobalt phthalocyanine, silver phthalocyanine, a metal-free phthalocyanine, a chemical derivative thereof, and combinations thereof.
 28. The lithium metal secondary battery of claim 1, wherein said cathode active material is in a form of nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a thickness or diameter from 0.5 nm to 100 nm.
 29. The lithium metal secondary battery of claim 28, wherein said nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn is coated with or embraced by a conductive protective coating selected from a carbon material, graphene, electronically conductive polymer, conductive metal oxide, or conductive metal coating. 